FIRE PROTECTION SEALXPERT FLAMECEASE FC100 FIRE PROTECTION COATING
SEALXPERT FLAMECEASE FC100 FIRE PROTECTION COATING
FEATURES
- Low installation cost
- High Durability Fire Tested under British Standard 476 Part 6, 7 & 20
- Contains no halogenated flame retardant
- Excellent lap shear, tensile, and compressive strength
- More specific to address complex issues with different resin types
APPLICATION
1. Ideal for use in:- Petrochemical plants
- Chemical processing plants
- Gas processing facilities
- Refinery facilities
- Pipe rack beams and columns
- Vessel skirts and supports
- Tank saddles
- Silo top
- Automotive/aircraft parts
2. Suitable for both interior and exterior applications
3. Suitable for onsite and offsite application
4. Apply by using brush or paint roller
5. Can be used as primer, fire protection coat and top coat, 3-in-1
6. May apply any epoxy base paint coating after FC100 base on personal preferences for aesthetic purpose
TECHNICAL DATA
| Gel time | 15 min |
| Gel to peak exotherm | 18 min |
| Total time to peak exotherm | 28 min |
| Peak exotherm temperature | 174°C (345 °F) |
| Barcol hardness | 49 |
| Tensile strength | 6672 psi (469 kg/cm 2) |
| Tensile modulus | 73 x 10 9 pa |
| Heat distortion temperature | 117°C (243 °F)@ 264 psi (19 kg/cm 2) |
| Adhesive strength | 1958 psi (138 kg/cm 2) |
| Tensile elongation | 2.8% |
| Flexural strength | 23931 psi (1683 kg/cm 2) |
| Flexural modulus | 6.8 x 10 9 pa |
| Fire Resistance | Recommended Coating Thickness (I-Beam) | Product Usage Per Coating |
| 1 hour fire protection | 1.0 mm thk / 2 coatings | 800 grams / m 2 |
| 2 hours fire protection | 1.5 mm thk / 3 coatings | 800 grams / m 2 |
| 3 hours fire protection | 3.5 mm thk / 7 coatings | 800 grams / m 2 |